CYCOLOY™ C1200HF resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YrPeR7_CYCOLOYC1200HFresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC+ABS, excellent flow/impact/high heat resistance. Low temperature ductility. For automotive, appliance and electrical components. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 19 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2280 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 57.2 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 5.0 | % | ASTM D638 |
| Fracture | 100 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2340 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 88.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 480 | J/m | ASTM D256 |
| 23°C | 590 | J/m | ASTM D256 |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 54.2 | J | ASTM D3763 |
| 23°C, Total Energy | 54.2 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 129 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 113 | °C | ASTM D648 |
| Vicat Softening Temperature | 130 | °C | ISO 306/B50 |
| CLTE - Flow (-40 to 40°C) | 7.2E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI | 105 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.19 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 - 80 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 250 - 290 | °C | |
| Middle Temperature | 255 - 295 | °C | |
| Front Temperature | 260 - 300 | °C | |
| Nozzle Temperature | 275 - 300 | °C | |
| Processing (Melt) Temp | 275 - 300 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.038 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ ABS 5007 | TER HELL PLASTIC GMBH | ABS | TEREZ ABS |
| NILENE® E20 K25T | Taro Plast S.p.A. | PP Copolymer | NILENE® |
| ASACLEAN™ EX | ASACLEAN - Sun Plastech Inc. | Proprietary | ASACLEAN™ |
| Karina IVORY PVC COMPOUND 550D35/ 1-AT-IS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina IVORY PVC COMPOUND 951-35/4-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |