SEPAZ™ LW8842FR
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | SEPAZ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YpPEAY_SEPAZ-LW8842FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SEPAZ LW8842FR is a GF/MF 35% reinforced modified PPO product. This product has high modulus, low warpage, and good processability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 125 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus 3 | 10500 | MPa | ASTM D790 |
| Flexural Strength 4 | 157 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 51 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 129 | °C | |
| 1.8 MPa, Unannealed | 123 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 250 to 300 | °C | |
| Middle Temperature | 260 to 305 | °C | |
| Front Temperature | 270 to 310 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 75.0 to 105 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL TP-FR-IM | Polymer Resources Ltd. | PBT | PRL |
| Vistek 1862 U | Visual Polymer Technologies, LLC | TP, Unspecified | Vistek |
| Vinnolit® K 301 NF | Vinnolit GmbH & Co. KG | PVC, Unspecified | Vinnolit® |
| ASTALAC™ ASA 305 | Marplex Australia Pty. Ltd. | ASA | ASTALAC™ |
| LNP™ THERMOCOMP™ RF00469S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |