Order Products : sales@su-jiao.com
Clearflex® FF D0
| Category: | VLDPE , Very Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Yo9Ubo_Clearflex-FF-D0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex FF D0 is a linear low density polyethylene, with antioxidants, suitable for blown film technology. The product is characterised by a very low density and high molecular weight. Films made with Clearflex FF D0 are highly transparent, have excellent sealing properties, mainly at low temperature, and outstanding mechanical performances. Main Application Clearflex FF D0 is recommended to produce stretch film and is used in blend or coextrusion because of its unique properties. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 10 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : Blown Film | 65.0 | MPa | |
| 1% Secant, TD : Blown Film | 70.0 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, Blown Film | 5.00 | MPa | |
| TD : Yield, Blown Film | 5.00 | MPa | |
| MD : Break, Blown Film | 50.0 | MPa | |
| TD : Break, Blown Film | 34.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, Blown Film | 450 | % | |
| TD : Break, Blown Film | 800 | % | |
| Dart Drop Impact 1(Blown Film) | 340 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD | 70.0 | kN/m | |
| TD | 150.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 65.0 | °C | ISO 306/A |
| Melting Temperature | 116 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, Blown Film) | 75 | ASTM D2457 | |
| Haze (Blown Film) | 7.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PP 2008/003 | Witcom Engineering Plastics B.V. | PP, Unspecified | Witcom PP |
| APEX® 4011 | Teknor Apex Company | PVC, Flexible | APEX® |
| DINALON® B1S25 G25XV0 | Grupo Repol | Nylon 6 | DINALON® |
| Kepamid® 2300SE | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |
| Lucky Enpla LGF2201F | Lucky Enpla Co LTD | PC+ABS | Lucky Enpla |