KOPA® KN333G30CR
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOPA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YneMxl_KOPA-KN333G30CR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KOPA® KN333G30CR is a Polyamide 66 (Nylon 66) product filled with 30% glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.70 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 186 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 7.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 9610 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 304 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648A | ||
| 0.45 MPa, Unannealed | 250 | °C | |
| 1.8 MPa, Unannealed | 247 | °C | |
| Peak Melting Temperature | 255 | °C | ASTM D3418 |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 21 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.60 | ASTM D150 | |
| Arc Resistance | 135 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNAMID® A A-SV25-ETK | Poly Plastic | Nylon 66 | TECHNAMID® A |
| Addisil™ 160 E | Momentive Performance Materials Inc. | Rubber | Addisil™ |
| TECACOMP® PP HTE black 4099 | Ensinger GmbH | PP, Unspecified | TECACOMP® |
| SQUARE® LIM1520-45A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |
| LG EVA EC33018 | LG Chem Ltd. | EVA | LG EVA |