XYLEX™ HX7509HP resin
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | XYLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YmMK6u_XYLEX-HX7509HP-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium flow, polycarbonate/Polyester alloy; contains mold release. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant. EtO and gamma sterilizable. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (265°C/2.16 kg) | 11.5 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.40 to 0.60 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.12 | % | |
| Equilibrium, 23°C, 50% RH | 0.050 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2150 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 60.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Break 3 | 63.0 | MPa | ASTM D638 |
| Break | 62.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.3 | % | ASTM D638 |
| Yield | 5.8 | % | ISO 527-2/50 |
| Break 5 | 140 | % | ASTM D638 |
| Break | 130 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2300 | MPa | ASTM D790 |
| -- 7 | 2260 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 92.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 95.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 70 | J/m | ASTM D256 |
| 23°C | 850 | J/m | ASTM D256 |
| -30°C 10 | 8.0 | kJ/m² | ISO 180/1A |
| -10°C 11 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 9.0 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 77.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 119 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 106 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 108 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 126 | °C | ASTM D1525, ISO 306/B120 11 14 |
| -- | 125 | °C | ISO 306/B50 |
| CLTE | |||
| Flow : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 6.8E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 6.8E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.23 | W/m/K | ISO 8302 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-2 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Haze (2540 µm) | 2.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 to 79.4 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 243 to 260 | °C | |
| Middle Temperature | 243 to 271 | °C | |
| Front Temperature | 249 to 271 | °C | |
| Nozzle Temperature | 249 to 271 | °C | |
| Processing (Melt) Temp | 249 to 271 | °C | |
| Mold Temperature | 43.3 to 60.0 | °C | |
| Back Pressure | 0.103 to 0.517 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Vent Depth | 0.013 to 0.020 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 mm |
| 14 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Network Polymers SAN 280 | Network Polymers, Inc. | SAN | Network Polymers SAN |
| Axiall PVC 8676 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| HAIPLEN EP30 G6 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| Kumho SBR 1739 | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho SBR |
| CYCOLAC™ FXS610SK resin | SABIC Innovative Plastics Europe | ABS | CYCOLAC™ |