Order Products : sales@su-jiao.com
Telcar® TL-1522G
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Telcar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YmIoTu_Telcar-TL-1522G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Telcar®TL-1522G is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is extrusion or injection molding. Typical application areas include:
|
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 26 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 68 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.3 | % | ASTM D955 |
| Transverse flow | 1.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance | ASTM D2228 | ||
| 1000 Cycles, 1000g, H-18 wheel | 65.0 | mg | ASTM D2228 |
| 1000 Cycles, 1000g, H-22 wheel | 86.0 | mg | ASTM D2228 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 1.86 | MPa | ASTM D412 |
| 300% strain | 2.90 | MPa | ASTM D412 |
| Tensile Strength (Break) | 5.79 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 690 | % | ASTM D412 |
| Tear Strength 1 | 31.5 | kN/m | ASTM D1004 |
| Compression Set | ASTM D395 | ||
| 23°C, 22 hr | 31 | % | ASTM D395 |
| 70°C, 22 hr | 74 | % | ASTM D395 |
| 100°C, 22 hr | 100 | % | ASTM D395 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | ||
| 23°C | 6.8E+18 | ohms·cm | ASTM D257 |
| 50°C | 2.1E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 35 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 171 - 193 | °C | |
| Middle Temperature | 177 - 199 | °C | |
| Front Temperature | 182 - 204 | °C | |
| Nozzle Temperature | 188 - 210 | °C | |
| Processing (Melt) Temp | 188 - 210 | °C | |
| Mold Temperature | 25.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 166 - 188 | °C | |
| Cylinder Zone 2 Temp. | 171 - 193 | °C | |
| Cylinder Zone 3 Temp. | 177 - 199 | °C | |
| Cylinder Zone 5 Temp. | 182 - 204 | °C | |
| Die Temperature | 190 - 210 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tufprene™ 126S | AKelastomers | SBS | Tufprene™ |
| NYLOY® UB-0010N G50N2N | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| NYLAFORCE® A 50 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | NYLAFORCE® |
| Delta ABS 780 | Delta Polymers | ABS | Delta |
| Di-Pak™ E-4701 | Hapco Inc. | TP, Unspecified | Di-Pak™ |