Ultraform® N 2320 0035 LEV
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultraform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YmIo5e_Ultraform-N-2320-0035-LEV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultraform N 2320 0035 LEV is designed to achieve low emission and smell |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 7.50 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2600 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 62.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 10 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 30 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 210 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 90.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 166 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.80 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 5.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 110 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 60.0 to 120 | °C | |
| Injection Pressure | 3.45 to 10.3 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Modified Plastics MPP-S1 | Modified Plastics, Inc. | PP, Unspecified | Modified Plastics |
| REVOLVE® N-228 | Matrix Polymers | Plastomer | REVOLVE® |
| LNP™ LUBRILOY™ U2000A compound | SABIC Innovative Plastics | PPA | LNP™ LUBRILOY™ |
| MAXATEL® AC90TFSi-BK | Pier One Polymers, Inc. | Acetal (POM) Copolymer | MAXATEL® |
| Sylvin 7868-90C Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |