DIAMALOY ABSPC 9901
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | DIAMALOY ABSPC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YkrqhE_DIAMALOY-ABSPC-9901.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DIAMALOY ABSPC 9901 is a Polycarbonate + ABS (PC+ABS) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1 | ASTM D1238 | ||
| 200°C/5.0 kg | 0.80 | g/10 min | |
| 230°C/3.8 kg | 3.9 | g/10 min | |
| Molding Shrinkage - Flow | 0.50 to 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2(Injection Molded) | 2670 | MPa | ASTM D638 |
| Tensile Strength 3(Yield) | 55.2 | MPa | ASTM D638 |
| Flexural Modulus | 2140 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 70.7 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 590 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.18 mm | 90.0 | °C | |
| 1.8 MPa, Annealed, 3.18 mm | 100 | °C | |
| Vicat Softening Temperature | 125 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 70 | % | |
| Suggested Max Regrind | 30 | % | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 235 to 265 | °C | |
| Front Temperature | 238 to 272 | °C | |
| Nozzle Temperature | 238 to 272 | °C | |
| Processing (Melt) Temp | 238 to 272 | °C | |
| Mold Temperature | 40.0 to 100 | °C | |
| Back Pressure | 0.345 to 1.03 | MPa |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type I |
| 3 . | 51 mm/min |
| 4 . | Method I (3 point load), Type I |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ProTherm® 4353 | Axiall Corporation | CPVC | ProTherm® |
| RheTech Polypropylene T20P250-731UV | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| apinat® A 75 | API SpA | TPE | apinat® |
| Compoceran E201 | Arakawa Chemical Industries, Ltd. | Epoxy | Compoceran |
| LNP™ LUBRICOMP™ UX06427 compound | SABIC Innovative Plastics | PPA | LNP™ LUBRICOMP™ |