Multilon® T-2850R
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | TEIJIN LIMITED |
| Trademark: | Multilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YkhVIi_Multilon-T-2850R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ABS polymer alloy |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/5.0 kg | 19.0 | cm³/10min | |
| 260°C/5.0 kg | 29.0 | cm³/10min | |
| Molding Shrinkage 1 | Internal Method | ||
| Across Flow : 4.00 mm | 0.50 to 0.70 | % | |
| Flow : 4.00 mm | 0.50 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 48.0 | MPa | |
| Break | 50.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 3.0 | % | |
| Break | 120 | % | |
| Flexural Modulus 2 | 2000 | MPa | ISO 178 |
| Flexural Stress 3 | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 65 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 120 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 95.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 111 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow | 8.0E-5 | cm/cm/°C | |
| Transverse | 8.0E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Mold shrinkage of Multilon will vary depending on its application thickness. |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PVC Film 165-J3 NT | Teknor Apex Company | PVC, Flexible | PVC Film |
| Zhongfa PP pp10 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| Flexathene® TP4308HR | LyondellBasell Industries | Polyolefin, Unspecified | Flexathene® |
| Escorene™ Ultra MV 02528EH2 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| King Pearl® FD-A | Loyal Chemical | PS (EPS) | King Pearl® |