HI-ZEX™ 1700J
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Prime Polymer Co., Ltd. |
| Trademark: | HI-ZEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YiigrR_HI-ZEX-1700J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HI-ZEX™ 1700J is a High Density Polyethylene product. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Primary characteristic: good stiffness. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.967 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 16 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 1300 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Injection Molded) | 29.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, Injection Molded) | 200 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 1300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 3.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 130 | °C | ISO 306 |
| Melting Temperature | 135 | °C | ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 2560.75 | RTP Company | PC+ABS | RTP |
| Shanghai Ofluorine PVDF T-1 | Shanghai Ofluorine Chemical Technology Co., Ltd | PVDF | Shanghai Ofluorine PVDF |
| Stylac™ 789 | Asahi Kasei Chemicals Corporation | AS | Stylac™ |
| NEFTEKHIM PP 9300M | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Cosmic DAP 306 | Cosmic Plastics, Inc. | DAP | Cosmic DAP |