Borealis PP VG602
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YiETkG_Borealis-PP-VG602.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VG602 is a 20% chemically coupled glass fibre reinforced polypropylene compound intended for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 75.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 4250 | MPa | ISO 178 |
| Flexural Stress | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 5.0 | kJ/m² | ISO 180/1A |
| 23°C | 9.8 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 140 | °C | ISO 75-2/Ae |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability (1.00 mm) | 100 | mm/min | ISO 3795 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperature: 40 - 80 °CMass Temperature: 230 - 280 °CBack Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 285 TFE 10 | RTP Company | Nylon 66 | RTP |
| SABIC® PPcompound 7540 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| TRIREX® Compound DMF3000S | Samyang Corporation | PC | TRIREX® Compound |
| CarmelStat™ CS 1115 | Carmel Olefins Ltd. | PP, Unspecified | CarmelStat™ |
| Axiall PVC 8923 | Axiall Corporation | PVC, Flexible | Axiall PVC |