Order Products : sales@su-jiao.com

Nylene® 721

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Custom Resins Group
Trademark:	Nylene®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Ygb7Zf_Nylene-721.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Medium-impact modified nylon for fast, easy molding

Parts molded from 721 have good impact strength right out of the mold without post conditioning

Suitable for applications such as clips, fasteners, and other parts where some initial flexibility and impact resistance is desired

Cylinder temperatures should be in the 450°F-500°F range.

General Information
Additive	Impact Modifier
Features	Good Impact Resistance Good Moldability Impact Modified
Uses	Fasteners
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.10	g/cm³	ASTM D792
Molding Shrinkage - Flow	1.4	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (23°C)	62.1	MPa	ASTM D638
Tensile Elongation (Break, 23°C)	200	%	ASTM D638
Flexural Modulus (23°C)	2170	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ASTM D256
-40°C	27	J/m
23°C	160	J/m

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, Unannealed	170	°C
1.8 MPa, Unannealed	62.8	°C
Peak Melting Temperature	221	°C	ASTM D3418

Injection	Nominal Value	Unit
Rear Temperature	232 to 260	°C
Middle Temperature	232 to 260	°C
Front Temperature	232 to 260	°C

Resin Grade	Manufacturer	Category	Trademark
RTP 2101 LF	RTP Company	PEI	RTP
TOTAL Polypropylene PPC 3645	TOTAL Refining & Chemicals	PP Impact Copolymer	TOTAL Polypropylene
KOPLA PP KPT1020	KOPLA Co., Ltd.	PP, Unspecified	KOPLA PP
Karina MB CONC OF PIGM BROWN -E 36/597-FC-LMP	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Paryls® PSU F3150GL30	Youju New Materials Co., Ltd.	PSU	Paryls®