NYCOA Polyamide 851
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YgGAZU_NYCOA-Polyamide-851.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 851 Nylon is a low viscosity Nylon 6 resin used for general-purpose injection molding and compounding. NYCOA 851 is available with custom additive packages; heat stabilizer, flame retardant, UV stabilizer as well as custom colors. Typical molding applications include gears, fasteners, and hardware items. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.2 | % | ASTM D955 |
| Transverse flow | 1.4 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.7 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 85.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 50 | % | ASTM D638 |
| Flexural Modulus 3 | 2600 | MPa | ASTM D790 |
| Flexural Strength 4 | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 185 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 68.3 | °C | ASTM D648 |
| Melting Temperature | 221 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 221 - 241 | °C | |
| Middle Temperature | 235 - 252 | °C | |
| Front Temperature | 246 - 260 | °C | |
| Nozzle Temperature | 254 - 266 | °C | |
| Processing (Melt) Temp | 249 - 266 | °C | |
| Mold Temperature | 76.7 - 87.8 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.138 - 0.517 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 16.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AIE PBT 3010F | Asia International Enterprise (Hong Kong) Limited | PBT | AIE PBT |
| Fasal® BIO 322 | Fasal Wood KG | Biodeg Polymers | Fasal® |
| Ghaed ABS/PC GAC 244 | Ghaed Basir Petrochemicals Co. | PC+ABS | Ghaed ABS/PC |
| OP - PC - Filled 20GF | Oxford Polymers | PC | OP - PC - Filled |
| OTECH PVC OW135-UL Approved | OTECH Corporation | PVC, Unspecified | OTECH PVC |