EcoPaXX® Q-Y
| Category: | Nylon 410 , Polyamide 410 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | EcoPaXX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Yg5I6H_EcoPaXX-Q-Y.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EcoPaXX® Q-Y is a Polyamide 410 (Nylon 410) material. It is available in Asia Pacific, Europe, or North America. Important attributes of EcoPaXX® Q-Y are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.08 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 1.2 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.8 | -- | % | ISO 62 |
| Calculated Bio-based Carbon Content | 66 | -- | % | ASTM D6866 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2500 | 1300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 65.0 | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 45 | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2400 | 1300 | MPa | ISO 178 |
| Flexural Stress | 95.0 | 50.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 9.0 | -- | kJ/m² | |
| 23°C | 41 | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 165 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 76.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 250 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 34 | 30 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 270 to 300 | °C | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3870H | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Softflex® 2910 | Network Polymers, Inc. | TPE | Softflex® |
| SLOVAMID® 66 GB 30 | Plastcom | Nylon 66 | SLOVAMID® 66 |
| Aaroprene® TFPP 2010 | Aaron Industries Corp. | PP, Unspecified | Aaroprene® |
| Geon™ Vinyl Flexible A8001 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |