Toraycon® 1101G-X08
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toraycon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YeFMEA_Toraycon-1101G-X08.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toraycon® 1101G-X08 is a Polybutylene Terephthalate (PBT) product filled with 35% glass bead\glass fiber. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.46 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 3.00 mm 1 | 0.80 | % | |
| Flow : 3.00 mm 2 | 0.30 | % | |
| Water Absorption (23°C, 24 hr) | 0.070 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, 23°C) | 57 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 8500 | MPa | ISO 527-2 |
| Tensile Stress (23°C) | 110 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 175 | MPa | ISO 178 |
| Coefficient of Friction 3 | 0.18 | ||
| Coefficient of Friction - vs. Metal 4 | 0.150 | Suzuki Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bar Flow Length 5(250°C, 1.00 mm) | 8.60 | cm | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 185 | °C | ISO 75-2/A |
| CLTE - Flow (-30 to 100°C) | 4.6E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | 26 | kV/mm | IEC 60243-1 |
| Dielectric Constant 6 | IEC 60250 | ||
| 23°C, 50 Hz | 3.50 | ||
| 23°C, 1 kHz | 3.40 | ||
| Dissipation Factor 7 | IEC 60250 | ||
| 23°C, 50 Hz | 2.0E-3 | ||
| 23°C, 1 MHz | 0.010 | ||
| Arc Resistance 8 | 100 | sec | IEC 60950 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.794 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | vs. Metal |
| 4 . | Without Lubrication |
| 5 . | 93 MPa |
| 6 . | 60% RH |
| 7 . | 60% RH |
| 8 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1102 FR | RTP Company | PET | RTP |
| VITAMIDE® AR8XBK6568 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| ABS Proquigel T | Proquigel | ABS | ABS Proquigel |
| ISOTHANE® 3075A | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyether | ISOTHANE® |
| KMI PP KM573-MJ | KMI Group, Inc. | PP Impact Copolymer | KMI PP |