Propafilm™ MTX90
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafilm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ye8i8o_Propafilm-MTX90.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Anti-Static Overwrapping Film Biaxially oriented polypropylene (BOPP) film co-extruded on both sides with heat sealable polyolefinic copolymers. MTX90 is suitable for high speed overwrapping of packets/cartons. The high level of anti-static protection enhances machine performance and minimizes dust attraction. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | Internal Method | ||
| Flow : 120°C, 1 min | 4.0 | % | |
| Across Flow : 120°C, 1 min | 3.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic, Outside/Outside | 0.25 | ||
| vs. Itself - Static, Outside/Outside | 0.35 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus 1 | ASTM D882 | ||
| 1% Secant, MD | 2400 | MPa | |
| 1% Secant, TD | 2400 | MPa | |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield | 200 | MPa | |
| TD : Yield | 185 | MPa | |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Break | 85 | % | |
| TD : Break | 85 | % | |
| Seal Strength 4 | 0.15 | N/mm | Internal Method |
| Seal Initiation Temperature 5 | 96.1 to 146 | °C | Internal Method |
| Oxygen Permeability (23°C, 0% RH) | 63 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water Vapor Transmission Rate | ASTM F1770 | ||
| 23°C, 85% RH | 1.2 | g/m²/24 hr | |
| 38°C, 90% RH | 7.3 | g/m²/24 hr | |
| Film Gauge | 90.0 | Internal Method | |
| Yield | 50.0 | m²/kg | Internal Method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 6 | 1.4E+10 | ohms | ASTM D257 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°) | 110 | ASTM D2457 | |
| Haze 7 | 2.2 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 10%/min |
| 2 . | 50%/min |
| 3 . | 50%/min |
| 4 . | 230°F; 1sec; 15lb/in² |
| 5 . | 2secs; 15lb/in² |
| 6 . | 77°F, 0%RH |
| 7 . | Wide angle, 2.5° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 FR BAC | RTP Company | Nylon 66 | RTP |
| Siloxane Masterbatch MB25-513 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| Glastic® 1605 | Bulk Molding Compounds, Inc. | Polyester, TS | Glastic® |
| Karina BROWN PVC COMPOUND 809-36/467-CRM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 4250-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |