RTP 105 TFE 15
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ye2ccF_RTP-105-TFE-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber - PTFE Lubricated |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.40 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8270 | MPa | ASTM D638 |
| Tensile Strength | 55.2 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.3 to 2.0 | % | ASTM D638 |
| Flexural Modulus | 6210 | MPa | ASTM D790 |
| Flexural Strength | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 64 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 210 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 157 | °C | |
| 1.8 MPa, Unannealed | 146 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 to 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 30 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 191 to 232 | °C | |
| Mold Temperature | 32.2 to 65.6 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 5014U | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| Dynaflex™ G7970-9001-02 | PolyOne Corporation | TPE | Dynaflex™ |
| ELASTOSIL® FLR 3905/60 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® FLR |
| LG ASA LI970 | LG Chem Ltd. | ASA | LG ASA |
| Petrothene® GA601033 | LyondellBasell Industries | LLDPE | Petrothene® |