Order Products : sales@su-jiao.com
Tenite™ Butyrate 572E3720012, Clear, Trsp
| Category: | CAB , Cellulose Acetate Butyrate |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Tenite™ Butyrate |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YdrsEt_Tenite-Butyrate-572E3720012-Clear-Trsp.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite™ cellulosic plastics are available in natural, clear, selected ambers or smoke transparents and black translucents. Color concentrates are available in let-down ratios from 10:1 to 40:1. ™Tenite™ Cellulose Acetate Butyrate 572-12 contains an odor mask lubricant and an ultra-violet inhibitor(UVI). It has a plasticizer level of 12%. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Water Absorption (23°C, 24 hr) | 1.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 87 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 33.8 | MPa | |
| Break, 23°C | 34.0 | MPa | |
| Tensile Elongation (Break, 23°C) | 23 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 98 | J/m | |
| 23°C | 350 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1 | ASTM D648 | ||
| 0.45 MPa, Annealed | 83.0 | °C | |
| 1.8 MPa, Annealed | 78.0 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Weight Loss on Heating 2(80°C) | 0.40 | % | ASTM D707 |
| Note Message | |
|---|---|
| 1 . | Conditioned 4 hours at 70°C (158°F) |
| 2 . | 72 hours |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HMP-305W (Roto) | Ravago Manufacturing Americas, LLC | LMDPE | Ravago Compounds |
| QR Resin QR-9006-GF40 | QTR, Inc. | Nylon 6 | QR Resin |
| VENELENE® 11PG4 | Poliolefinas Internacionales, C.A. (Polinter) | LLDPE | VENELENE® |
| Borealis PP BJ368MO | Borealis AG | PP Copolymer | Borealis PP |
| Perlast® G75B | Precision Polymer Engineering Ltd. | Perfluoroelastomer | Perlast® |