NORYL PPX™ PPX7115F resin
| Category: | PPE+PS+PP , Polyphenylene Ether + PS + PP |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL PPX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YdWcKk_NORYL-PPX-PPX7115F-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High modulus/impact/heat PPE+PP |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.988 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 14 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.60 to 0.70 | % | |
| Across Flow : 3.20 mm | 0.60 to 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1240 | MPa | ASTM D638 |
| -- | 1380 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 35.9 | MPa | ASTM D638 |
| Yield | 35.0 | MPa | ISO 527-2/50 |
| Break 3 | 34.5 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield 4 | 8.0 | % | ASTM D638 |
| Break 5 | 130 | % | ASTM D638 |
| Break | 75 | % | ISO 527-2/50 |
| Flexural Modulus 6(50.0 mm Span) | 1380 | MPa | ASTM D790 |
| Flexural Strength 7(Yield, 50.0 mm Span) | 51.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 530 | J/m | ASTM D256 |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 30.0 | J | |
| 23°C, Total Energy | 37.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 113 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 8 | 116 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 85.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 86.7 | °C | ASTM D1525 9 |
| -- | 131 | °C | ISO 306/A50 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 1.6E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 9.7E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 65.6 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 227 to 277 | °C | |
| Middle Temperature | 238 to 282 | °C | |
| Front Temperature | 249 to 288 | °C | |
| Nozzle Temperature | 260 to 288 | °C | |
| Processing (Melt) Temp | 260 to 288 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 mm |
| 9 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT4900-33UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| ESTOPLAST EP 7035 | Ester Industries Ltd. | PET | ESTOPLAST EP |
| HiFill® PA12 GF15 L | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Hylon® N4033HL | Ravago Manufacturing Americas, LLC | Nylon 66/6 | Hylon® |
| OnForce™ LFT LF6600-5017 Grey | PolyOne Corporation | Nylon 66 | OnForce™ LFT |