XENOY™ 1102 resin
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YdVrhL_XENOY-1102-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced PC/polyester alloy. Excellent low temperatue impact/chemical resistance to automotive fluids. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Specific Volume | 0.835 | cm³/g | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.80 to 1.0 | % | |
| Across Flow : 3.20 mm | 0.80 to 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 54.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 150 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 1970 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 82.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 640 | J/m | |
| 0°C | 690 | J/m | |
| 23°C | 800 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 110 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 90.6 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 50 to 80 | % | |
| Rear Temperature | 243 to 266 | °C | |
| Middle Temperature | 249 to 271 | °C | |
| Front Temperature | 254 to 277 | °C | |
| Nozzle Temperature | 254 to 271 | °C | |
| Processing (Melt) Temp | 260 to 277 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.013 to 0.020 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SPESIN® KP270HL | Kolon Plastics, Inc. | PBT | SPESIN® |
| NuSil MED-4174 | NuSil Technology | Rubber | NuSil |
| Lushan EV1050G1 | Guangzhou Lushan New Materials Co., Ltd | EVA | Lushan |
| MAJORIS CE141 - 8229 | AD majoris | Polyolefin, Unspecified | MAJORIS |
| Sylvin 7833-90 Grey 9193 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |