ISPLEN® PC 272 AV
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | REPSOL |
| Trademark: | ISPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YdGUXT_ISPLEN-PC-272-AV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene copolymer compound, with 20% calcium carbonate and high melt flow rate. ISPLEN® PC272 AV shows good impact strength an a medium rigidity. It gives high stiffness, and a low warpage and shrinkage behaviour. This product is UV stabilised an antistatic formulated. APPLICATIONS Aesthetic applications which require good gloss surface.
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 14 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | 1.1 to 1.3 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 66 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 22.5 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 3.5 | % | ISO 527-2 |
| Flexural Modulus | 1650 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 1.3 | kJ/m² | |
| -20°C | 1.5 | kJ/m² | |
| 0°C | 2.0 | kJ/m² | |
| 23°C | 3.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -40°C | 42 | kJ/m² | |
| -20°C | 53 | kJ/m² | |
| 0°C | 70 | kJ/m² | |
| 23°C | 140 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 5.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 81.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 149 | °C | ISO 306/A120 |
| -- | 85.0 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 150x100x3mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 5012 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| Generic Nylon 6 - Talc | Generic | Nylon 6 | Generic |
| INEOS PP H12Z-00 | INEOS Olefins & Polymers USA | PP Homopolymer | INEOS PP |
| TECHNYL® A 50X1 GREY 2607 | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® |
| LNP™ LUBRICOMP™ KFL23LH compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |