SCHULADUR® A1 GF 30 HF FR 1
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULADUR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Yd9P7A_SCHULADUR-A1-GF-30-HF-FR-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High flow flame retardant halogenated PBT/PET compound reinforced with 30% glass fiber; without PBDE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.68 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 54.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 148 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/1A/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | ISO 179/1eU |
| 23°C | 46 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 219 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 198 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 218 | °C | ISO 306/A50 |
| -- | 190 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | ISO 3795 | ||
| 0.750mm, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| 1.50mm, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| 3.00mm, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 0.750 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 1.50 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 3.00 mm | V-0 5VA | UL 94, IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.750 mm | 960 | °C | IEC 60695-2-12 |
| 1.50 mm | 960 | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm | 675 | °C | IEC 60695-2-13 |
| 1.50 mm | 675 | °C | IEC 60695-2-13 |
| 3.00 mm | 675 | °C | IEC 60695-2-13 |
| Oxygen Index | 34 | % | ISO 4589-2 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applicationsCharacteristic propertiesSCHULADUR possesses good rigidity, cold impact strength, dimensional stability and high heat deflection temperature. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 10 | % | |
| Hopper Temperature | 70.0 | °C | |
| Rear Temperature | 230 | °C | |
| Middle Temperature | 245 | °C | |
| Front Temperature | 260 | °C | |
| Nozzle Temperature | 260 | °C | |
| Processing (Melt) Temp | 240 - 255 | °C | |
| Mold Temperature | 80.0 - 110 | °C | |
| Injection Pressure | 100 - 140 | MPa | |
| Injection Rate | Moderate | ||
| Holding Pressure | 40.0 - 70.0 | MPa | |
| Back Pressure | 5.00 - 10.0 | MPa | |
| Cushion | 2.00 - 5.00 | mm | |
| Vent Depth | 0.020 | mm | |
| Screw Speed | mm/sec |
| Injection instructions |
|---|
| PredryingA dehumidifying dryer has to be used for drying. Unless a drying hopper is in use, material for no more than one hours processing should be placed in the hopper.ReprocessingUp to 20% regrind may be used, in which case use of additional stabilization is recommended as a safety precaution. Use only well dried regrind.Shut downAfter breaks >2 minutes purge with fresh material. For shut down purge with polyolefin. For breaks in production reduce the temperature to 210° C.FinishingSCHULADUR is suitable for machining. Varnishing, printing, gluing and embossing can be carried out using commercially available products after pretreatment. This is often achieved by washing the surface with an organic solvent.It can be laser marked without special Additives. For improved contrast use specific laser printable types. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® 64C-R | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Baydur® 263 IMR (600 g/m² Glass Weight) | Covestro - PUR | PUR-MDI | Baydur® |
| Polifil® PP GFPPCC-20 | The Plastics Group | PP Homopolymer | Polifil® PP |
| Hifax CA 60 G NERO | LyondellBasell Industries | PP Copolymer | Hifax |
| Sylvin 6168-80 Yellow 405 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |