Plexiglas® Diffuse™ V045-68207
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Altuglas International of Arkema Inc. |
| Trademark: | Plexiglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YcRkTe_PlexiglasDiffuseV04568207.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plexiglas® Diffuse™ V045-68207 is a thermoplastic acrylic resin formulated for injection molding and extrusion applications in the LED lighting market. It is characterized by an excellent balance of transmission and hiding performance. It exhibits a textured surface when extruded. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 - 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 88 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3300 | MPa | ASTM D638 |
| Tensile Strength (Break) | 69.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 15 | % | ASTM D638 |
| Flexural Modulus | 3000 | MPa | ASTM D790 |
| Flexural Strength (Break) | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 36 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1 | ASTM D648 | ||
| 0.45 MPa, annealed | 101 | °C | ASTM D648 |
| 1.8 MPa, annealed | 97.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 106 | °C | ASTM D1525 2 |
| -- | 100 | °C | ASTM D1525 3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm) | 89.0 | % | ASTM D1003 |
| Haze (2000 µm) | > 100 | % | ASTM D1003 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ASTM Classification | PMMA 0131T1V1 | ASTM D788 |
| Note Message | |
|---|---|
| 1 . | Annealing Cycle: 16 hours @ 90°C (194°F) |
| 2 . | 速率 A (50°C/h), 压 力1 (10N) |
| 3 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPRO HDPE RH120 | Rondo Plast AB | HDPE | REPRO |
| Baypreg® F 315 (10 mm Glass Mat Reinforced Sandwich) | Covestro - PUR | PUR, Unspecified | Baypreg® |
| Clariant Nylon 6/6 66G13-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| CP PRYME® Polycarbonate PC100RULUV-10M Black | Chase Plastics Services Inc. | PC | CP PRYME® Polycarbonate |
| Petrothene® NA940094 | LyondellBasell Industries | LDPE | Petrothene® |