Edistir® ICE S 900
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Edistir® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YbzatH_Edistir-ICE-S-900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Very high environmental stress cracking resistant (VH ESCR) HIPS. ICE S 900 exhibits high toughness and excellent chemical resistance to oils, fats and chemical agents and in particular to cyclopentane. Suitable for extrusion / thermoforming and injection moulding. Designation: Thermoplastics ISO 2897-PS-I,G,093-03-07-12 Applications Designed for inner liners and frames for refrigerators where cyclopentane is used as blowing agent for insulating polyurethane foams. ICE S 900 significantly improves the wall thickness distribution in thermoforming and allows to optimize the thickness of the original extruded sheet. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 - 0.70 | % | Internal method |
| Water Absorption (23°C, 24 hr) | < 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1450 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 17.5 | MPa | ISO 527-2/50 |
| Fracture | 25.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 70 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 11 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 92.0 | °C | ISO 306/B50 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.17 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.5E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 7.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 65 | kV/mm | IEC 60243-1 |
| Dielectric Constant (50 Hz) | 2.50 | IEC 60250 | |
| Dissipation Factor (50 Hz) | 3.0E-4 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Internal testig) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 - 260 | °C | |
| Mold Temperature | 20.0 - 60.0 | °C |
| Injection instructions |
|---|
| Predrying normally not required |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 210 - 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VECTOR® 4211A | Dexco Polymers LP | SIS | VECTOR® |
| NEXT REGRIND PA66 ST801-300RG | NEXT Specialty Resins, Inc. | Nylon 66 | NEXT REGRIND |
| GAPEX® RPP10EA53BK | Ferro Corporation | PP Homopolymer | GAPEX® |
| Karina STRAW COLOR CONCENTRATE 38/ 49-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1-8840 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |