LNP™ THERMOCOMP™ MB006HS compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Yas5HL_LNPTHERMOCOMPMB006HScompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP MB006HS is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound MB-1006 HS HC Product reorder name: MB006HS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2590 | MPa | ASTM D638 |
| Tensile Strength (Break) | 28.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 23 | % | ASTM D638 |
| Flexural Modulus | 2040 | MPa | ASTM D790 |
| Flexural Strength | 41.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 21 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 230 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 63.9 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene RCC120-01 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Witcom PP 2007/117 | Witcom Engineering Plastics B.V. | PP, Unspecified | Witcom PP |
| Arak HDPE BL6 | Shazand (Arak) Petrochemical Corporation | HDPE | Arak HDPE |
| Axiall PVC MP-6585 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Generic POP | Generic | POP | Generic |