ENGAGE™ 7447
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YaKeu3_ENGAGE-7447.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENGAGE™ 7447 is a high ethylene butene melt flow, low density copolymer designed for use alone or in combination with our other elastomers to provide the tailored solutions in polymer modifications applications. Main Characteristics:
Applications:
Complies with Government / Industry Standards:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.865 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 7 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 sec, Compression Molded | 64 | ||
| Shore D, 1 sec, Compression Molded | 12 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1(Compression Molded) | 1.70 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Compression Molded) | 2.40 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 550 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : Compression Molded | 7.80 | MPa | |
| 2% Secant : Compression Molded | 7.60 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 24.8 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -53.0 | °C | Internal Method |
| Melting Temperature (DSC) 5 | 35.0 | °C | Internal Method |
| Peak Crystallization Temperature (DSC) | 29.0 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | Die C |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V974 BLK580 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| ICORENE® N1018 | ICO Polymers EMEA, A Division of A. Schulman | EVA | ICORENE® |
| Lustran® ABS LK197 | INEOS ABS (USA) | ABS | Lustran® ABS |
| OmniLon™ PA6/6 GR13 FR All Colors | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
| Plasmer 1065BM/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |