NORYL™ 6390C resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YZgE8Q_NORYL-6390C-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PPO |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 280°C/10.0 kg | 8.00 | cm³/10min | |
| 280°C/21.6 kg | 14.0 | cm³/10min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2550 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 81.0 | MPa | |
| Break | 76.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 5.6 | % | |
| Break | 8.0 | % | |
| Flexural Modulus 1 | 2600 | MPa | ISO 178 |
| Flexural Stress | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2 | ISO 180/1A | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 64.0 mm Span) | 170 | °C | ISO 75-2/Af |
| Glass Transition Temperature | 196 | °C | DSC |
| Vicat Softening Temperature | 192 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LDM 720 | Marco Polo International, Inc. | LDPE | MARPOL® |
| Braskem PP R7022-50NA | Braskem America Inc. | PP Random Copolymer | Braskem PP |
| Delrin® 311DP BK402 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| ESTADIENE 3008 MT | Cossa Polimeri S.r.l. | ABS | ESTADIENE |
| ESTOPLAST EP 5010RD14 | Ester Industries Ltd. | PBT | ESTOPLAST EP |