Clariant Nylon 6/6 PA-111
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Clariant Corporation |
| Trademark: | Clariant Nylon 6/6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YZ1ZWh_Clariant-Nylon-6-6-PA-111.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clariant Nylon 6/6 PA-111 is a polyamide 66 (nylon 66) material,. This product is available in North America and is processed by injection molding. The main features of Clariant Nylon 6/6 PA-111 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.7 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.2 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 82.7 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 60 | % | ASTM D638 |
| Flexural Modulus | 2830 | MPa | ASTM D790 |
| Flexural Strength | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 235 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 76.7 | °C | ASTM D648 |
| Melting Temperature | 255 | °C | |
| CLTE - Flow | 7.7E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 18 | kV/mm | ASTM D149 |
| Arc Resistance (3.05 mm) | 90.0 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.710 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 266 - 293 | °C | |
| Middle Temperature | 266 - 293 | °C | |
| Front Temperature | 266 - 293 | °C | |
| Processing (Melt) Temp | 266 - 288 | °C | |
| Melt Temperature (Aim) | 274 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Cushion | 3.18 - 6.35 | mm |
| Injection instructions |
|---|
| Injection Pressure: Use minimum pressure to achieve 95% fill during the boost inj. phase.Hold Pressure: 30% to 75% of injection pressure.Mold Temp. Target: 180°FScrew Speed Target: 75 RPM |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 49MK40 | SABIC Americas, Inc. | PP Impact Copolymer | SABIC® PP |
| Tecopet® PT70 GR30 NL100 XA20 | Eurotec Engineering Plastics | PET | Tecopet® |
| Ultradur® B 4406 G4 | BASF Corporation | PBT | Ultradur® |
| AIE PPO 9010F-S120E | Asia International Enterprise (Hong Kong) Limited | PPE+PS | AIE PPO |
| Bionate® 90A | DSM Biomedical Inc. | PC+TPU | Bionate® |