Borealis PE CC8207

Category:	LDPE , Low Density Polyethylene
Manufacturer:	Borealis AG
Trademark:	Borealis PE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	YY851A_Borealis-PE-CC8207.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
CC8207 is a pigmented Extrusion Coating grade. The incorporated pigments give the required light and UV-barrier especially in those applications where instead of Al-foil, barrier polymers like EVOH are used. The pigments and concentration are carefully selected so that the grey color has a very close Al-foil appearance. The overall light penetration can be reduced remarkably especially in the wavelength area of 400-700 nm. As such CC8207 can be used as light and UV barrier material. CC8207 is based on standard LDPE coating material therefore normal LDPE extrusion coating settings can be selected. However, as for pigmented products in general, extrusion temperatures above 315 - 320°C should be avoided. In case that CC8207 is stored for long period pre-drying before extrusion is recommended.

Message

CC8207 is a pigmented Extrusion Coating grade. The incorporated pigments give the required light and UV-barrier especially in those applications where instead of Al-foil, barrier polymers like EVOH are used. The pigments and concentration are carefully selected so that the grey color has a very close Al-foil appearance. The overall light penetration can be reduced remarkably especially in the wavelength area of 400-700 nm. As such CC8207 can be used as light and UV barrier material.
CC8207 is based on standard LDPE coating material therefore normal LDPE extrusion coating settings can be selected. However, as for pigmented products in general, extrusion temperatures above 315 - 320°C should be avoided.
In case that CC8207 is stored for long period pre-drying before extrusion is recommended.

General Information
Features	Good UV Resistance Low Density Recyclable Material
Uses	Coating Applications
Forms	Pellets
Processing Method	Extrusion Extrusion Coating

Physical	Nominal Value	Unit	Test Method
Density	0.920	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	6.0	g/10 min	ISO 1133

Additional Information	Nominal Value	Unit	Test Method
Pigment Content	7.1	%	Internal Method
Total Neck-In	7.20	cm	Internal Method

Extrusion	Nominal Value	Unit	Test Method
Maximum Coating Speed	7.5	m/sec	Internal Method
Maximum Coating Weight	7.00	g/m²	Internal Method
Melt Temperature	315 to 320	°C

Resin Grade	Manufacturer	Category	Trademark
Unipren® Elastomers B3 NTLA010 55A UP310	Petropol Industry and Trade of Polymers LTDA	PP+EPDM	Unipren® Elastomers
Xuchuan XCW-6425DH	Xuchuan Chemical (Suzhou) Co., Ltd	PUR, Unspecified	Xuchuan
Formolene® L42009E2	Formosa Plastics Corporation, U.S.A.	LLDPE	Formolene®
Latene® 7 TR-V2	LATI S.p.A.	PP Homopolymer	Latene®
PPR POM17	Premier Plastic Resins, Inc.	Acetal (POM) Homopolymer	PPR