LNP™ THERMOCOMP™ RF00AS compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YY7zAH_LNP-THERMOCOMP-RF00AS-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* RF00AS is a compound based on Nylon 66 resin containing 50% Glass Fiber. Added features of this material include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound RF-100-10 HS Product reorder name: RF00AS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 1.2 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.34 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.40 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.74 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 17700 | MPa | ASTM D638 |
| -- | 14000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 198 | MPa | ASTM D638 |
| Break | 194 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 2.4 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 12500 | MPa | ASTM D790 |
| -- | 14500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 312 | MPa | ASTM D790 |
| -- | 300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 150 | J/m | ASTM D256 |
| 23°C 2 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1600 | J/m | ASTM D4812 |
| 23°C 3 | 66 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 12.2 | J | ASTM D3763 |
| -- | 3.90 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 253 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | > 240 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 2.7E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 2.8E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 4.3E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 4.4E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC-UV2-D(f1)-(color)-1 | Polymer Resources Ltd. | PC | PRL |
| Toughblend® PBT-1600 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PBT | Toughblend® |
| TPV Elastoprene® N55A-E | ELASTORSA Elastomeros Riojanos S.A. | PP+EPDM | TPV Elastoprene® |
| ESTOPLAST EP 4030GY27 | Ester Industries Ltd. | PBT | ESTOPLAST EP |
| Sylvin 9302-70 FU White 1327 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |