Toyolac® 470Y MH1
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Toray Plastics (Malaysia) Sdn. Bhd. |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YX3d08_Toyolac-470Y-MH1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toyolac® 470Y MH1 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific or Europe. Important attributes of Toyolac® 470Y MH1 are:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.60 to 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 1 | 39.0 | MPa | ASTM D638 |
| Yield | 44.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 2 | 20 | % | ASTM D638 |
| Break | > 10 | % | ISO 527-2/50 |
| Flexural Modulus 3 | 1960 | MPa | ASTM D790 |
| Flexural Strength | |||
| -- 4 | 62.0 | MPa | ASTM D790 |
| -- 5 | 66.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 170 | J/m | |
| 23°C, 12.7 mm | 150 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 110 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 104 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ LW8842FR | Mando Advanced Materials Co., Ltd. | PPE+PS | SEPAZ™ |
| THERMOLAST® K TF1SNT (Series: FC/S) | KRAIBURG TPE | TPE | THERMOLAST® K |
| EPO-TEK® 302-3M | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Hyundai EP Breathable AT880H/2102 | HYUNDAI EP Co., Ltd. | Polyolefin, Unspecified | Hyundai EP Breathable |
| Karina BLACK PVC COMPOUND 701-DA-48/ 18-A-BZ (**) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |