POLYFLAM® RIPP 4000 E Datasheet,PP Copolymer,A. Schulman Europe-SHANGHAI SUSHENG

Message
Unfilled flame-retardant PP-Copolymer, Extrusion grade, halogenfree

General Information
Features	Copolymer Workability, good Halogen-free Flame retardancy
Processing Method	Extrusion Injection molding
Resin ID (ISO 1043)	PP FR(51)

Physical	Nominal Value	Unit	Test Method
Density	1.06	g/cm³	ISO 1183/A
Melt Volume-Flow Rate (MVR) (230°C/2.16 kg)	2.00	cm³/10min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1600	MPa	ISO 527-2/1A/1
Tensile Stress			ISO 527-2/1A/50
Yield	15.0	MPa	ISO 527-2/1A/50
Fracture	12.0	MPa	ISO 527-2/1A/50
Tensile Strain (Yield)	3.7	%	ISO 527-2/1A/50
Nominal Tensile Strain at Break	100	%	ISO 527-2/1A/50
Flexural Modulus ¹	1600	MPa	ISO 178
Flexural Stress ²			ISO 178
4.4% strain	24.5	MPa	ISO 178
3.5% strain	24.2	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	3.0	kJ/m²	ISO 179/1eA
23°C	7.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	35	kJ/m²	ISO 179/1eU
23°C	No Break		ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	94.0	°C	ISO 75-2/B
1.8 MPa, not annealed	55.0	°C	ISO 75-2/Af
Vicat Softening Temperature
--	138	°C	ISO 306/A50
--	57.0	°C	ISO 306/B50

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flammability Classification			IEC 60695-11-10, -20
0.8 mm	V-0		IEC 60695-11-10, -20
1.6 mm	V-0		IEC 60695-11-10, -20
3.2 mm	V-0		IEC 60695-11-10, -20
Glow Wire Flammability Index			IEC 60695-2-12
0.75 mm	960	°C	IEC 60695-2-12
1.5 mm	960	°C	IEC 60695-2-12
3.0 mm	960	°C	IEC 60695-2-12
Glow Wire Ignition Temperature			IEC 60695-2-13
0.75 mm	700	°C	IEC 60695-2-13
1.5 mm	700	°C	IEC 60695-2-13
3.0 mm	700	°C	IEC 60695-2-13

Additional Information
1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications

Injection	Nominal Value	Unit
Drying Temperature	70	°C
Drying Time	2.0 - 4.0	hr
Processing (Melt) Temp	180 - 210	°C
Mold Temperature	40 - 80	°C
Injection Pressure	80.0 - 120	MPa
Injection Rate	Slow-Moderate
Holding Pressure	40.0 - 90.0	MPa
Back Pressure	5.00 - 10.0	MPa
Screw Speed		mm/sec

Injection instructions
PredryingPredrying at 70°C for 2-4 hours is recommended as a precaution.ReprocessingAddition of regrind is normally possible, but it must be tested in each case regarding the percentage and requirements of the article. Thermal damage during first processing depends on processing parameters and the geometry of flow path and article.Shut downAvoid long melt residence time. Purge with base polymer or with polyolefines.FinishingMachining is usually possible.

Injection instructions

PredryingPredrying at 70°C for 2-4 hours is recommended as a precaution.ReprocessingAddition of regrind is normally possible, but it must be tested in each case regarding the percentage and requirements of the article. Thermal damage during first processing depends on processing parameters and the geometry of flow path and article.Shut downAvoid long melt residence time. Purge with base polymer or with polyolefines.FinishingMachining is usually possible.

Note Message
1 .	2.0 mm/min
2 .	2.0 mm/min

Category:	PP Copolymer , Polypropylene Copolymer
Manufacturer:	A. Schulman Europe
Trademark:	POLYFLAM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	YWqsVq_POLYFLAMRIPP4000E.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RheTech Polypropylene GC10P200-00	RheTech, Inc.	PP Copolymer	RheTech Polypropylene
Nipol® DN302	Zeon Chemicals L.P.	NBR	Nipol®
Durez® 33005	SBHPP	Phenolic	Durez®
Sylvin 8940-80 Orange 580	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Durethan® BKV 30 XTS1 901510	LANXESS GmbH	Nylon 6	Durethan®