| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Arkema |
| Trademark: | Orevac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YWnwVl_Orevac-18750.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OREVAC® 18750 is a coextrusion coating adhesive based on a maleic anhydride modified polypropylene resin. It is available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polyolefin. Applications OREVAC® 18750 is a tie resin to be used in extrusion coating and extrusion lamination technologies. It has been designed to develop adhesion in these processes onto substrates like aluminum foil (*), paper or PP films and in coextrusion with resins like PP and PA. OREVAC® 18750 exhibits excellent processing properties, particularly regarding drawability, neck-in and melt stability. In addition to adhesive properties, the special formulation of OREVAC® 18750 allows to design aluminum lids for PP or PP coated cups and containers with controlled opening forces. (*) Adhesion performance to aluminum foil is strongly dependant on thermal conditions in the laminator. Standard conditions of coating onto cold aluminum foil require using a specific post heating treatment in which the OREVAC layer must be molten again. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 35 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (0.0250 mm) | 500 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield, 0.0250 mm) | 16.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, 0.0250 mm) | > 700 | % | ASTM D638, ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 121 | °C | ISO 306/A, ASTM D1525 1 |
| Melting Temperature | 160 | °C | ISO 11357-3 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Cylinder Zone 1 Temp. | 200 to 220 | °C | |
| Cylinder Zone 2 Temp. | 220 to 250 | °C | |
| Cylinder Zone 3 Temp. | 250 to 275 | °C | |
| Cylinder Zone 4 Temp. | 275 | °C | |
| Die Temperature | 275 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP301R | LyondellBasell Industries | PP Homopolymer | Moplen |
| Moplen EP310D | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Fainplast PVC PH 58/AL | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| elitel UE3230 | UNITIKA Plastics Division | TPC-ET | elitel |
| HANWHA EVA 1815 | Hanwha Chemical | EVA | HANWHA EVA |