RTP EMI 2563 FR
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YWgT1g_RTP-EMI-2563-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stainless Steel Fiber - EMI/RFI Shielding - Electrically Conductive - Flame Retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 - 0.60 | % | ASTM D955 |
| Moisture Content | 0.020 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay | sec | FTMS 101C 4046.1 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4140 | MPa | ASTM D638 |
| Tensile Strength | 66.9 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.0 - 3.0 | % | ASTM D638 |
| Flexural Modulus | 4140 | MPa | ASTM D790 |
| Flexural Strength | 123 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 37 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 370 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 110 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | < 1.0E+4 | ohms | ASTM D257 |
| -- | < 1.0E+3 | ohms | ESD STM11.11 |
| Volume Resistivity | < 1.0 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, ** Values per RTP Company testing. | V-0 | UL 94 | |
| 3.00 mm, ** Values per RTP Company testing. | 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -28.9 | °C | |
| Processing (Melt) Temp | 243 - 274 | °C | |
| Mold Temperature | 51.7 - 93.3 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Use a reverse barrel profile. Remove hopper magnets. Allow 4 - 5 shots to properly disperse the conductive fibers. The surface finish should have a silver streaking appearance, not clumps.Use a reverse barrel profile. To maximize fiber length, the following injection barrel, screw, and tip designs should be followed. L/D ratio 16/1 - 22/1, Compression ratio 2:1, Flight depth 0.200 in (5 mm) minimum, in feed section, Screw diameter 0.65 - 0Remove hopper magnets.Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BY36BK6595 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| CROSSVINIL RCF/AZ GRIGIO | Crosspolimeri S.p.A. | PVC, Unspecified | CROSSVINIL |
| MAXAMID™ PA66M32T-NC010 | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| INDURE™ X225-UV SILH | LyondellBasell Industries | Polyolefin, Unspecified | INDURE™ |
| Techsil® TIM11123 (GB) | Techsil Limited | Silicone Rubber, RTV-1 | Techsil® |