PENTALLOY BP (HV) H natural
| Category: | Nylon 6+PP , Polyamide 6 + PP |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTALLOY BP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YWIwPR_PENTALLOYBPHVHnatural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High viscosity PA6+PP-alloy (extrusion grade), non-reinforced, heat stabilised, resistant to corrosion |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.04 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.9 | -- | % | ISO 294-4 |
| Flow | 1.4 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 4.5 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.3 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2700 | 1800 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 61.0 | 46.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ||||
| Yield | 4.4 | 9.0 | % | ISO 527-2/50 |
| Fracture | 26 | > 40 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 13 | 25 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 140 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 80.0 | -- | °C | ISO 75-2/A |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.6 mm | HB | -- | UL 94 | |
| 3.2 mm | HB | -- | UL 94 |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 - 0.13 | % | |
| Cylinder Zone 1 Temp. | 245 - 260 | °C | |
| Cylinder Zone 2 Temp. | 250 - 265 | °C | |
| Cylinder Zone 3 Temp. | 255 - 270 | °C | |
| Cylinder Zone 4 Temp. | 260 - 270 | °C | |
| Cylinder Zone 5 Temp. | 265 | °C | |
| Melt Temperature | 240 - 280 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Flontech® FT-PPTA20-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| INEOS HDPE K38-20-160 | INEOS Olefins & Polymers USA | MDPE | INEOS HDPE |
| Karina CLEAR PVC COMPOUND 80/221-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ RFL36SXS compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| LUVOCOM® 19-7748 VP | Lehmann & Voss & Co. | Nylon 46 | LUVOCOM® |