Celcon® M90-34
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celcon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YW6hp4_Celcon-M90-34.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Celcon® M90-34 is a specially formulated injection moldable grade of acetal copolymer for the appliance market targeted at resisting staining while providing a balance of properties. Chemical abbreviation according to ISO 1043-1: POM |
| General Information | |
|---|---|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 2.2 | % | ASTM D955 |
| Transverse flow | 1.8 | % | ASTM D955 |
| Vertical flow direction | 1.8 | % | ISO 294-4 |
| Flow direction | 2.2 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.75 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2550 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield, 23°C | 60.7 | MPa | ASTM D638 |
| Yield | 63.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 11 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 2450 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.4 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 6.2 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 110 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 100 | °C | ISO 75-2/A |
| Melting Temperature 1 | 165 | °C | ISO 11357-3, ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 190 | °C | |
| Front Temperature | 180 - 190 | °C | |
| Nozzle Temperature | 190 - 200 | °C | |
| Processing (Melt) Temp | 180 - 200 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 180 to 200°CZone 4 Temperature: 190 to 200°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® 700 314 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| AVP™ KLL10CP | SABIC Innovative Plastics | PC | AVP™ |
| EVERLON® TP-40D | Ever Polymer Co., Ltd. | SEBS | EVERLON® |
| Flontech® FT-1-1L | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Kuraray Poval® PVA 117H | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |