ELEVATE™ EF437
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | ELEVATE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YVBMeh_ELEVATE-EF437.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Westlake EF437 resin is a 2.5% EVA copolymer designed for films that require excellent optical and strength properties. This Kosher compliant resin has excellent heat sealing characteristics and low temperature brittleness properties. Application/Uses: High Clarity Packaging Light and Medium Duty Produce Bags Linear Blend Component for Sealing and Clarity |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 2.5 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| secant modulus 1 | ASTM D882 | ||
| 1% secant, MD : 32 µm, blown film | 138 | MPa | ASTM D882 |
| 1% secant, TD : 32 µm, blown film | 152 | MPa | ASTM D882 |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Broken, 32 µm, blown film | 24.0 | MPa | ASTM D882 |
| TD : Broken, 32 µm, blown film | 17.0 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Broken, 32 µm, blown film | 350 | % | ASTM D882 |
| TD : Broken, 32 µm, blown film | 700 | % | ASTM D882 |
| Dart Drop Impact 4(32 µm, Blown Film) | 150 | g | ASTM D1709A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 31.8 µm, Blown Film) | 79 | ASTM D2457 | |
| Haze (31.8 µm, Blown Film) | 3.3 | % | ASTM D1003 |
| Additional Information |
|---|
| Test specimens for blown film: nominal thickness 1.25 mils; blow up ratio 2.5:1, die gap 35 mils. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 199 | °C |
| Extrusion instructions |
|---|
| Melt temperatures of 360° F - 390° F are recommended for Westlake Chemical EF437 with blow-up ratios of 1.5:1 or higher. |
| Note Message | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | Test run at 23°C (73°F) and 50% relative humidity |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® 21ZLV | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| EPO-TEK® P1011S | Epoxy Technology Inc. | PI, TS | EPO-TEK® |
| SD POLYCA™ CF5201V | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |
| SQUARE® LIM3900-20A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |
| LEXAN™ HF1130 resin | SABIC Innovative Plastics | PC | LEXAN™ |