Retpol® 3029 UV3
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YUKQK6_Retpol-3029-UV3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extron 3029 UV3 is a 43% talc and glass fibre reinforced coupled polypropylene compound. It is a medium to high flow injection moulding grade developed for components requiring minimal shrinkage with high heat deflection temperatures, high rigidity and good impact strength. It is UV stabilized for continuous outdoor use. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.20 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 109 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 82 | ||
| Shore D, 15 sec, 3.00 mm | 76 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 90.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 2.0 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 7730 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 67 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 450 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.00 mm | 162 | °C | |
| 1.8 MPa, Unannealed, 3.00 mm | 152 | °C | |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SER-200 | SHIN-A T&C | Epoxy | SHIN-A |
| Tenite™ Propionate 383A2R30009 Natural, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| NYCOA Polyamide 2063 | Nycoa (Nylon Corporation of America) | Nylon 66/6 | NYCOA Polyamide |
| DENIBLEND F | Vamp Tech | PC+ABS | DENIBLEND |
| Polyrocks EP8400X125F-1 | Polyrocks Chemical Co., Ltd | XLPE | Polyrocks |