DILAMID® 66 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Dilaplast S.p.A. |
| Trademark: | DILAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YUIZhW_DILAMID-66-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DILAMID®66 NATURAL is a polyamide 66 (nylon 66) material,. This product is available in Europe, and the processing method is injection molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 1.5 - 1.9 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 20 | % | ISO 527-2 |
| Flexural Modulus | 2.50 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 6.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 220 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| Available also in version WW (Elastomer modified free conditioning) and ELT (Elastomer modified high impact).HDT A (1.80 MPa) Unannealed, ISO 75A-1, 2: >80°CComparative Track Index, IEC 60112: >500 V |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 100 | °C | |
| Drying Time | 2.0 - 8.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 250 - 280 | °C | |
| Middle Temperature | 260 - 290 | °C | |
| Front Temperature | 270 - 300 | °C | |
| Nozzle Temperature | 265 - 295 | °C | |
| Processing (Melt) Temp | 270 - 300 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Retpol® 7575 HS UV1 | PolyPacific Pty. Ltd. | PP, Unspecified | Retpol® |
| Axiall PVC 28850 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Elastamax™ HTE 1101 | PolyOne Corporation | SBC | Elastamax™ |
| LG ASA LI970HF | LG Chem Ltd. | ASA | LG ASA |
| LNP™ THERMOCOMP™ DC0041PQ compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |