Retpol® 9020 HS
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YUAzE3_Retpol-9020-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Retpol 9020 HS is a medium to high flow flame retardant homopolymer polypropylene compound. It has been developed to meet the requirements of UL 94 V-2 flammability rating and AS/NZS 60695.2.12 960°C glow- wire flammability index, whilst still maintaining the property balance between impact strength and rigidity of polypropylene. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.928 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 to 1.9 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 35.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 110 | % | ASTM D638 |
| Flexural Modulus | 1500 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 25 | J/m | ASTM D256 |
| Unnotched Izod Impact | 800 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 95.0 | °C | ASTM D648 |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-2 | ||
| 3.00 mm | V-2 | ||
| Glow Wire Flammability Index (3.00 mm) | 960 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 5 | % | |
| Processing (Melt) Temp | 180 to 225 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® AGV HW 30 Black | Radici Plastics | Nylon 66 | Radilon® |
| CP PRYME® Polypropylene PPC100-20M | Chase Plastics Services Inc. | PP Copolymer | CP PRYME® Polypropylene |
| Hanwha Total PP TH54I | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| LEXAN™ LUX9612G resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| Jackdaw PP ER14BK8003 | Jackdaw Polymers | PP, Unspecified | Jackdaw PP |