SABIC® PP 523K
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YTrFSo_SABIC-PP-523K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® PP 523K is a nucleated grade and provides therefore high stiffness, more transparency and gloss if compared to conventional homopolymers. Moreover, it is formulated with a combined processing and antistatic package. SABIC® PP 523K is used for thermoformed food and drink containers. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus 1 | 1900 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 3.5 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/A50 |
| -- | 87.0 | °C | ISO 306/B50 |
| Additional Information |
|---|
| Anti block agent: NoSlip agent: NoAnti static agent: YesNucleating agent: YesAnti gas fading: No |
| Note Message | |
|---|---|
| 1 . | Method I (three-point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bergadur™ PB400 G30 UF UV | PolyOne Corporation | PBT | Bergadur™ |
| ALCUDIA® LDPE 2303-FG | REPSOL | LDPE | ALCUDIA® LDPE |
| Flontech® FT-CAR33-GR2-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Envir® PA66G25HL-BK0101 | Barnet | Nylon 66 | Envir® |
| LNP™ COLORCOMP™ 203RC compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |