Message
LUVOCOM®105-8763 is a thermoplastic elastomer (TPE) material containing a carbon fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 105-8763 are: Conductivity Electrostatic protection Typical application areas include: House engineering/industrial accessories Handle

General Information
Filler / Reinforcement	Carbon fiber reinforced material
Features	Conductivity Electrostatic discharge protection
Uses	Handle Roller Shell
Appearance	Black

Physical	Nominal Value	Unit	Test Method
Density	0.980	g/cm³	ISO 1183
Molding Shrinkage	0.20 - 0.50	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.30	%

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	70		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	100	MPa	ISO 527-2
Tensile Stress (Break)	5.00	MPa	ISO 527-2
Tensile Strain (Yield)	5.0	%	ISO 527-2

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	No Break		ISO 179/1fU

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	< 1.0E+4	ohms	IEC 60093
Insulation Resistance		ohms	IEC 60167

Injection	Nominal Value	Unit
Drying Temperature - Desiccant Dryer	85.0	°C
Drying Time - Desiccant Dryer	2.0 - 3.0	hr
Suggested Max Moisture	0.010	%
Rear Temperature	160 - 185	°C
Middle Temperature	170 - 190	°C
Front Temperature	175 - 195	°C
Nozzle Temperature	180 - 200	°C
Processing (Melt) Temp	200	°C
Mold Temperature	25.0 - 55.0	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.01%, otherwise molecular degradation may occur. As the material absorbs water very rapidly, originally sealed containers should only be opened immediately before processing. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.01%, otherwise molecular degradation may occur. As the material absorbs water very rapidly, originally sealed containers should only be opened immediately before processing. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	YTTAEL_LUVOCOM-105-8763.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Mirakutoran® TPU E690	Japan Mirakutoran Inc.	TPU Alloy	Mirakutoran® TPU
Selvol™ 823	Sekisui Chemical Company, Ltd.	PVOH	Selvol™
TOLEN H030 GP	SIBUR, LLC	PP Homopolymer	TOLEN
3M™ Dyneon™ Perfluoroelastomer PFE 90Z	3M Advanced Materials Division	Perfluoroelastomer	3M™ Dyneon™ Perfluoroelastomer
Sylvin 9077-90C BLACK	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin