Grivory® HTV-6H1 black 9205
| Category: | Nylon 6I/6T , Polyamide 6I/6T Copolymer |
| Manufacturer: | EMS-GRIVORY |
| Trademark: | Grivory® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YTB0tb_Grivory-HTV-6H1-black-9205.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Grivory® HTV-6H1 black 9205 is a Polyamide 6I/6T Copolymer (Nylon 6I/6T) material filled with 60% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Grivory® HTV-6H1 black 9205 are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.78 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.50 | -- | % | |
| Flow | 0.10 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 3.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.2 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 360 | 360 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 23000 | 22500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 260 | 250 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.5 | 1.5 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 10 | kJ/m² | |
| 23°C | 11 | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 75 | 75 | kJ/m² | |
| 23°C | 75 | 75 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | 290 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 215 | -- | °C | ISO 75-2/C |
| Continuous Use Temperature | Internal Method | |||
| -- 1 | 150 | -- | °C | |
| -- 2 | 250 | -- | °C | |
| Melting Temperature 3 | 325 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.5E-5 | -- | cm/cm/°C | |
| Transverse | 4.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | 30 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (0.800 mm) | HB | -- | IEC 60695-11-10, -20 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA6T/6I, MH, 12-220, GF60 | -- | ISO 1874 |
| Note Message | |
|---|---|
| 1 . | Long Term |
| 2 . | Short Term |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PVC Film 06-A0370R-87NT | Teknor Apex Company | PVC, Flexible | PVC Film |
| TEREZ PA 6.6 7500 GF 35 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| AA-Recoplast A1H1 | Smart Kemi SIA | HDPE | AA-Recoplast |
| Altuglas® V 045 I | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| POLYFLON™ D-46 | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |