Formolene FORMAX® L91507A
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Formosa Plastics Corporation, U.S.A. |
| Trademark: | Formolene FORMAX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YSwUcg_Formolene-FORMAX-L91507A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Formolene FORMAX® L9 is a superior strength linear low density hexene copolymer polyethylene made using a gas-phase process. Film mechanical properties are comparable to premium strength LLDPE film resins. Formolene FORMAX® L9 is formulated with slip and antiblock for use in high performance film applications offering excellent extrusion processing and outstanding impact strength and tear resistance. Films exhibit good optical properties. Formolene FORMAX® L9 meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact. Suggested Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.915 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, Blown Film | 10.5 | MPa | |
| TD : Yield, 25 µm, Blown Film | 10.5 | MPa | |
| MD : Break, 25 µm, Blown Film | 39.3 | MPa | |
| TD : Break, 25 µm, Blown Film | 34.5 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 670 | % | |
| TD : Break, 25 µm, Blown Film | 880 | % | |
| Dart Drop Impact (25 µm, Blown Film) | 540 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, Blown Film | 470 | g | |
| TD : 25 µm, Blown Film | 650 | g | |
| Seal Initiation Temperature 1(51 µm) | 103 | °C |
| Note Message | |
|---|---|
| 1 . | Temperature at which 2 lb/in heat seal strengh is achieved. Lako Tool SL-10 Heat Seal/Hot Tack Tester, 0.5 sec dwell, 40 psi bar pressure, peel speed 10 in./min. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA ABS 4134 70/35 (China) | MBA Polymers | ABS | MBA ABS |
| Topilene® J842 | Hyosung Corporation | PP Impact Copolymer | Topilene® |
| Hifax EP3080G | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Lumiloy® GP2300 | LG Chem Ltd. | PPE+PS | Lumiloy® |
| Sylvin 9302-70FU Brown 7307 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |