Desmopan® DP 1485A
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Desmopan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YSRxmv_Desmopan-DP-1485A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extrusion- and injection molding grade; suitable for extrusion blow molding; very large processing window; high melt stability; Beads; Application; Bellows; Hoses, non-reinforced; Profiles; Injection molded engineering parts |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.22 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A, 23°C | 84 | ||
| Shore D, 23°C | 33 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | DIN 53504 | ||
| Break, 23°C | 45.0 | MPa | |
| 100% Strain, 23°C | 5.20 | MPa | |
| 300% Strain, 23°C | 9.00 | MPa | |
| Tensile Strain 2(Break, 23°C) | 700 | % | DIN 53504 |
| Abrasion Resistance (23°C) | 30.0 | mm³ | ISO 4649-A |
| Tensile Storage Modulus | ISO 6721-1,-4 | ||
| -20°C | 290 | MPa | |
| 20°C | 31.0 | MPa | |
| 60°C | 21.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Resilience (23°C) | 44 | % | ISO 4662 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 3(23°C) | 63 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 19 | % | |
| 70°C, 24 hr | 45 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Processing (Melt) Temp | 220 to 240 | °C | |
| Mold Temperature | 20.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Melt Temperature | 200 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 200 mm/min |
| 2 . | 200 mm/min |
| 3 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRISAN NX3200 | Formosa Plastics Corporation | SAN | TAIRISAN |
| ALTECH® PA6 A 4020/100 MR20 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| GAPEX® RPP30EB59HB NATURAL | Ferro Corporation | PP Homopolymer | GAPEX® |
| EPO-TEK® H20E-HC | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| KOPPS® S25G40 | Kolon Plastics, Inc. | PPS | KOPPS® |