Styrolux® 3G46
| Category: | SBC , Styrene Butadiene Block Copolymer |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Styrolux® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YSHOsH_Styrolux-3G46.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Styrolux® 3G46 is a clear styrene-butadiene copolymer (SBC) developed specifically for sheet- and film extrusion and for thermoformed articles. Styrolux 3G46 is designed for improved performance in blends with general-purpose polystyrene, providing parts with an excellent balance of transparency and toughness. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 11 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (200°C/5.0 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.65 | % | ASTM D955 |
| -- | 0.30 to 1.0 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.070 | % | ASTM D570, ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore D | 75 | ASTM D2240 | |
| Shore D | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 1640 | MPa | ASTM D638 |
| -- | 1550 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 25.5 | MPa | ASTM D638 |
| Yield, 23°C | 27.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield, 23°C | 2.0 | % | ISO 527-2 |
| Break | 220 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | 180 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 1330 | MPa | ASTM D790 |
| -- | 1550 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 27.2 | MPa | ASTM D790 |
| 5.0% Strain | 31.0 | MPa | |
| -- | 31.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 | |
| Notched Izod Impact | |||
| 23°C | 32 | J/m | ASTM D256 |
| -30°C | 2.0 | kJ/m² | ISO 180/A |
| 23°C | 3.0 | kJ/m² | ISO 180/A |
| Instrumented Dart Impact (Total energy) | 20.1 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 75.6 | °C | ASTM D648 |
| 0.45 MPa, Annealed | 75.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 58.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 87.8 | °C | ASTM D1525 1 |
| -- | 81.0 | °C | ISO 306/A50 |
| -- | 51.0 | °C | ISO 306/B50 |
| CLTE - Flow | |||
| -- | 1.3E-4 | cm/cm/°C | ASTM D696 |
| -- | 6.0E-5 to 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | > 1.0E+14 | ohms | ASTM D257 |
| -- | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Constant | |||
| 1.00 mm, 1 MHz | 2.50 | ASTM D150 | |
| 100 Hz | 2.50 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 2 | 1.573 | ASTM D542, ISO 489 | |
| Transmittance (550 nm) | 91.0 | % | ASTM D1003 |
| Haze | 0.20 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 180 to 250 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| 2 . | Sodium D Line |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILPURAN® 8030/40 | Wacker Chemie AG | Silicone | SILPURAN® |
| DiaAlloy TP-30E | Mitsubishi Rayon America Inc. | PC | DiaAlloy |
| Gallonprene® GP410-5003 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Kynar Flex® 2850 WR | Arkema | PVDF | Kynar Flex® |
| LNP™ THERMOCOMP™ MX99432 compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |