SABIC® HDPE M100053C
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YS2RXg_SABIC-HDPE-M100053C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC®HDPE M100053C is a high density polyethylene product,. It can be processed by injection molding and is available in Europe. SABIC®HDPE M100053C applications include hats/caps/corks and food contact applications. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.953 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 10 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 28 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 190°C/2.16 kg | 13.0 | cm³/10min | ISO 1133 |
| 190°C/5.0 kg | 37.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec, Compression Molded) | 60 | ISO 868 | |
| Ball Indentation Hardness (H 132/30) | 48.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1050 | MPa | ISO 527-2/1BA/1 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00mm, molded | 26.0 | MPa | ISO 527-2/1BA/50 |
| Fracture, 2.00mm, molded | 14.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | 400 | % | ISO 527-2/1BA/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 460 | MPa | ISO 899-1 |
| 1000 hr | 230 | MPa | ISO 899-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 3.0 | kJ/m² | ISO 180/1A |
| 23°C | 3.0 | kJ/m² | ISO 180/1A |
| Tensile Impact Strength | 33.0 | kJ/m² | ISO 8256/1B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 70.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 44.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 122 | °C | ISO 306/A50 |
| -- | 68.0 | °C | ISO 306/B50 |
| Additional Information |
|---|
| ESCR, SABIC Method, Determined in Rhodacal-DS10 at 60°C, 2 N/mm², thickness 3mm: 30hrTensile Impact Elongation at Break, ISO 8256, Type 1, Method B: 1.4%Tensile Impact Maximum Tension, ISO 8256, Type 1, Method B: 34 MPaMelting Point, DIN 53765, Tmelt(top) at 5°C/min: 130°CEnthalpy Change, DIN 53765: 200J/g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next PC CX-01WH | Next Polymers Ltd. | PC | Next PC |
| Cellophane™ 500MS | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Europrene® SOL T 6434 | Versalis S.p.A. | SBS | Europrene® |
| ISOTAL™ C13F | SABIC Innovative Plastics Europe | Acetal (POM) Copolymer | ISOTAL™ |
| MAJORIS CETAL DG215 | AD majoris | Acetal (POM) Copolymer | MAJORIS |