NOTIO™ PN-0040
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Mitsui Chemicals America, Inc. |
| Trademark: | NOTIO™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YRzBli_NOTIO-PN-0040.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NOTIO™ is a flexible, low density, transparent elastomer with excellent heat resistance. The resin is not cross- linked and demonstrates superior elasticity. NOTIO's crystalline and amorphous structure (morphology) is controlled at the nano scale, allowing for the realization of properties that cannot be achieved with conventional elastomers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.868 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 86 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 42.0 | MPa | Internal Method |
| Tensile Strength 2(Break) | 22.0 | MPa | Internal Method |
| Tensile Elongation 3(Break) | 750 | % | Internal Method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Set 4(150% Strain) | 16 | % | Internal Method |
| Compression Set 5 | Internal Method | ||
| 23°C, 24 hr | 25 | % | |
| 70°C, 24 hr | 75 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -28.0 | °C | ASTM D746 |
| Glass Transition Temperature | 100 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (2000 µm, Compression Molded) | 5.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | JIS K7113-2 |
| 2 . | JIS K7113-2 |
| 3 . | JIS K7113-2 |
| 4 . | JIS K7113-2, 0.3 mm |
| 5 . | JIS K7113-2, 12 mm, 25% compression |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ HP0339C20L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| ARC ARC5009 | ARC Resin Corporation | Acetal (POM) Copolymer | ARC |
| InnoTuf® TP-4052 | Innovative Polymers, Inc. | TSU | InnoTuf® |
| Plyophen 43204 | Durez Corporation | Phenolic | Plyophen |
| Stanyl® WTP81 | DSM Engineering Plastics | Nylon 46 | Stanyl® |