Solef® 41308
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Solef® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YRoccN_Solef-41308.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Solef® 41308/0001 PVDF is specifically developed for coextrusion. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.78 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 230°C/2.16 kg | 6.0 to 8.0 | g/10 min | |
| 230°C/5.0 kg | 18 to 24 | g/10 min | |
| Water Absorption 1(23°C, 24 hr) | < 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2(23°C) | 1900 | MPa | ASTM D638 |
| Tensile Strength 3 | ASTM D638 | ||
| Yield, 23°C | 48.0 | MPa | |
| Break, 23°C | 30.0 | MPa | |
| Tensile Elongation 4(Yield, 23°C) | 7.0 | % | ASTM D638 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.31 | ||
| vs. Itself - Static | 0.32 | ||
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-10 Wheel) | 8.00 | mg | ISO 5470-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5(23°C) | 8.5 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 169 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 136 | °C | ASTM D3418 |
| Crystallization Heat | 51.6 | J/g | ASTM D3418 |
| Heat of Fusion 6 | 52.7 | J/g | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | Method 1 |
| 2 . | 1.0 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 4 mm thick, 2 m/s |
| 6 . | 80°C to end of melting |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sipolprene® 35195 B | SIPOL S.p.A | TPC-ET | Sipolprene® |
| AIE PC/ABS A2200FR-5008 | Asia International Enterprise (Hong Kong) Limited | PC+ABS | AIE PC/ABS |
| GAPEX® RPP30EA70BK | Ferro Corporation | PP Homopolymer | GAPEX® |
| Geon™ Vinyl Wire & Cable WR3790BL | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| Kapex C062 | Ginar Technology Co., LTD. | PC | Kapex |