SABIC® PPcompound 7603
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YRo1UV_SABIC-PPcompound-7603.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 7603 is a mineral filled modified polypropylene. This material combines high scratch resistance with a good stiffness and impact. Addtionally the material offers a high flow and low density. This material has a broad processing window and good esthical performance. Typical applications include automotive interior parts such as instrument panels, lower and upper dashboard, door panels and trim. SABIC® PPcompound 7603 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 1.2 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 22.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 20.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 500 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 1500 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 4.0 | kJ/m² | |
| 0°C, Injection Molded | 7.0 | kJ/m² | |
| 23°C, Injection Molded | 15 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 100 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 120 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 8.0E-5 | cm/cm/°C | |
| 23 to 80°C | 1.2E-4 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201 GB 20 | RTP Company | Nylon 66 | RTP |
| Vinnolit® SA 1062/7 | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| Vydyne® ECO366 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| EverGlide® 1908 | Polymer Dynamix | Nylon 6 | EverGlide® |
| Karina YELLOW PVC COMPOUND -E 530-02/167-A-IS-SD (C900) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |